Accurate and fast diffusible Hydrogen measurements
Thermal Desorption Mass Spectrometry (TDMS )
Accurate and rapid diffusible hydrogen measurements allow you to avoid embrittlement, hydrogen-induced cracking and other costly failures.
Hydrogen-induced damage is a wide-spread and dreaded phenomenon. During welding, hydrogen is generated from the dissociation of water vapor (e.g. humidity) or hydrocarbons in the welding arc, and the molten metal can rapidly pick up hydrogen. Once in the metal, hydrogen atoms can diffuse swiftly inside the microstructure of the metal. Diffusible hydrogen causes hydrogen induced cracking (also known as cold or delayed cracking), where components fail under the influence of mechanical stress - suddenly and without prior indication. Thus, diffusible hydrogen is critical to assess because of embrittlement, hydrogen induced or assisted cracking (HIC/HAC) or hydrogen delayed fracture among other damaging effects.
The G4 PHOENIX DH, utilizing carrier gas warm extraction for a rapid and automatic determination of diffusible hydrogen in a wide variety of matrices.
Hydrogen induced cracking and embrittlement is a dangerous phenomenon. Although high-strengths steels and oxygenated copper grades are particular susceptible to hydrogen embrittlement, an uptake of diffusible hydrogen affects many more metals but depends to a large extend on the environmental and process conditions, like ambient moisture. There is a risk to introduce hydrogen in every mechanical, thermal and galvanic manufacturing step, especially during welding and soldering.
The rapid method applied by the G4 PHEONIX can deliver results in less than 30 min, whereas traditional methods require multiple days. Thus, it is the only method allowing a feasible pre-welding testing for diffusible hydrogen. This allows users to optimize their process to avoid costly failures, before they are done.
|G4 PHOENIX||Thermal conductivity detector with reference channel and adjustable gain amplifier||Reliable, adjustable ranges, drift free|
|G4 PHOENIX MS||Mass spectrometer, m/z range 1-100 amu, single quadrupole, optimized EI source and channeltron detector||Unique mass spectrometry performance|
|Infrared heated||IR furnace uop to 900 ºC, i.d. of quartz tube 30 mm, water cooled, optinal thermocouple kit for direct sample temperature readings||Precise temperature control, flexible heating programms, accepts large samples|
|Resistance Heated (option)||Additional resistance heated furnace up to 1100 ºC, i.d. of quartz tube 18 mm||Residual hydrogen in multi-phase duplex steels|
|Carrier Gas||Nitorgen 99.995% purity, min. 2 bar (~50 psi), 99.9990% purity for trace analysis||Pre-cleaning using regenerateable molecular sieve|
|Calibration Gas||With pure gases (H2 or He1) or certified mixtures (each component 99.999% purity), automatic gas dose calibration system with 10 individual volumes||Easy, precise gas calibration without standards, traceable to p, T, V|
|Cooling Water||1 l/min @ 3 bar (44 psi)||Fast cool down, standard tap water compatible, water-saving design with water-stop valve, chiller also possible|
|G4 PHOENIX||230 VAC (± 10 %), 50-60 Hz, 2200 VA||Industry standard power and current configurations|
|Mass Spectrometer||230 VAC, 50-60 Hz, 250 VA|
|Dimension & Weight|
|G4 PHOENIX||630 x 700 x 670 mm (W x D x H), weight ~ 50 kg|
|Mass Spectrometer||630 x 640 x 480 mm (W x D x H), weight ~ 60 kg|